NDLI: Explaining Porosity Formation in Underwater Wet Welds

Content Provider	The American Society of Mechanical Engineers (ASME) Digital Collection
Author	Pe´rez-Guerrero, Faustino Liu, Stephen
Copyright Year	2007
Abstract	Macroscopic porosity in underwater wet welds is one of the main defects that deteriorate the mechanical properties of the wet welded joints. It is well established that weld metal porosity is a function of pressure, thus water depth. However, the mechanism of porosity formation is not well understood, therefore the problem is not yet mitigated to acceptable levels, particularly at water depths close to and beyond 100 m. To purposely produce porous welds similar to those obtained in wet welding, bead-on-plate (BOP) welds were deposited in air with gas metal arc welding (GMAW) with no shielding gas, with autogenous gas tungsten arc welding (GTAW) and GTAW with cold wire feed using insufficient shielding gas (8 CFH). During welding with both processes, oxygen from the atmosphere readily reacts with the alloying elements in the molten tip of the wire and in the weld pool. Under these conditions, droplets that detach from the wire electrode will generally contain a gas bubble, which is transported into the weld metal. These two welding processes were selected because there is no slag produced in the process. Slag slows down the cooling while giving enough time for degassing to occur, as in the case of shielded metal arc welding (SMAW) in air. Even with insufficient shielding gas, the autogenous GTAW welds did not exhibit porosity because there was no metal addition in the form of droplets. However, when a wire was fed into the arc, droplets detached from the wire in the oxidizing atmosphere transported gas into the weld pool, manifested as external and internal weld metal porosity. Similarly, the GMAW BOP welds exhibited internal porosity. When quenched in water, the droplets that detached from the electrode in these oxidizing conditions exhibited internal voids. Metal transfer analysis performed on the GMAW BOP welds associated short circuiting mode with large droplets and high porosity contents (10 pct.). Conversely, small droplets are expected to transport less gas and produce less porosity. Proof of concept welds using the pulsed current GMAW (GMAW-P) process resulted in higher droplet detachment frequency, smaller droplets and a low number of short circuiting droplets. Even though a few short circuiting events were still present, the GMAW-P process drastically reduced porosity to only 0.2 pct. Chemical reaction between oxygen and carbon generates CO gas at the bottom surface of the droplets in flat welding position, this gas ascends and is partially trapped inside the droplet. However, when the welding torch and base metal are rotated 90 degrees or in horizontal welding position, the CO gas generated escapes. Consequently there is no CO bubble in the pendant droplet or porosity in the weld metal. Wet welds were made with pulsed current using AWS E6010 electrode at a pressure equivalent to 50 m water depth. Porosity was reduced from 3.9 with constant current to 2.5 pct with pulsed current. Even when porosity was reduced with pulsed current, higher pulse frequency needs to be tested along with different peak and background current values to further reduce porosity. Flux covered electrodes with ferro-manganese, ferro-titanium and boron additions were extruded for wet welding. These electrodes produced wet welds with an average porosity of 1.2 pct., which could be further reduced to 0.85 pct. by better control of the arc at the beginning side of the weld.
Sponsorship	Ocean, Offshore and Arctic Engineering Division
Starting Page	249
Ending Page	257
Page Count	9
File Format	PDF
ISBN	0791842703
DOI	10.1115/OMAE2007-29696
e-ISBN	0791837998
Volume Number	Volume 4: Materials Technology; Ocean Engineering
Conference Proceedings	ASME 2007 26th International Conference on Offshore Mechanics and Arctic Engineering
Language	English
Publisher Date	2007-06-10
Publisher Place	San Diego, California, USA
Access Restriction	Subscribed
Subject Keyword	Gas metal arc welding Water Oxygen Cooling Welding Metals Mechanical properties Chemical reactions Gas tungsten arc welding Wire Arc welding Pressure Carbon Electrodes Slags Base metals Welded joints Bubbles Boron Drops Titanium Porosity Ferromanganese
Content Type	Text
Resource Type	Article

Sl.	Authority	Responsibilities	Communication Details
1	Ministry of Education (GoI), Department of Higher Education	Sanctioning Authority	https://www.education.gov.in/ict-initiatives
2	Indian Institute of Technology Kharagpur	Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project	https://www.iitkgp.ac.in
3	National Digital Library of India Office, Indian Institute of Technology Kharagpur	The administrative and infrastructural headquarters of the project	Dr. B. Sutradhar bsutra@ndl.gov.in
4	Project PI / Joint PI	Principal Investigator and Joint Principal Investigators of the project	Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon
5	Website/Portal (Helpdesk)	Queries regarding NDLI and its services	support@ndl.gov.in
6	Contents and Copyright Issues	Queries related to content curation and copyright issues	content@ndl.gov.in
7	National Digital Libarray of India Club (NDLI Club)	Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach	clubsupport@ndl.gov.in
8	Digital Preservation Centre (DPC)	Assistance with digitizing and archiving copyright-free printed books	dpc@ndl.gov.in
9	IDR Setup or Support	Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops	idr@ndl.gov.in

The Effect of Base Metal and Core Rod Carbon Content on Underwater Wet Weld Porosity

Study of Porosity Location in Fresh Water Wet Welds

Effect of Nickel on Toughness of Underwater Wet Welds

Study of “Re-Melt” Temper Bead and Polarity Effects on Porosity in the Under Freshwater Wet Welds

Designing Shielded Metal Arc Consumables for Underwater Wet Welding in Offshore Applications

Effect of Pulsed Current Gas Tungsten Arc Welding Parameters on Microstructure of Titanium Alloy Welds

Characterizing Metal Arc Welding Under Oil (MAW-UO)

Metal-Cored Welding GMAW Consumables Development for Girth Welding of X-100 Pipe

Vertical-Up Gas Tungsten Arc Welding of Ti6Al4V Alloy and Characterization

Explaining Porosity Formation in Underwater Wet Welds

Similar Documents

The Effect of Base Metal and Core Rod Carbon Content on Underwater Wet Weld Porosity

Study of Porosity Location in Fresh Water Wet Welds

Effect of Nickel on Toughness of Underwater Wet Welds

Study of “Re-Melt” Temper Bead and Polarity Effects on Porosity in the Under Freshwater Wet Welds

Designing Shielded Metal Arc Consumables for Underwater Wet Welding in Offshore Applications

Effect of Pulsed Current Gas Tungsten Arc Welding Parameters on Microstructure of Titanium Alloy Welds

Characterizing Metal Arc Welding Under Oil (MAW-UO)

Metal-Cored Welding GMAW Consumables Development for Girth Welding of X-100 Pipe

Vertical-Up Gas Tungsten Arc Welding of Ti6Al4V Alloy and Characterization

Explaining Porosity Formation in Underwater Wet Welds