Author Lee, Dongyun
Source SpringerLink
Content type Text
Publisher The Korean Institute of Metals and Materials
File Format PDF
Copyright Year ©2006
Language English
Subject Domain (in DDC) Technology ♦ Engineering & allied operations
Subject Keyword intermetallic alloys ♦ casting ♦ solution heat treatment ♦ oxidation ♦ mechanical properties ♦ Metallic Materials ♦ Operating Procedures, Materials Treatment ♦ Magnetism, Magnetic Materials ♦ Engineering Thermodynamics, Heat and Mass Transfer ♦ Characterization and Evaluation of Materials ♦ Continuum Mechanics and Mechanics of Materials
Abstract Solution heat treatment is employed in an attempt to improve oxidation and mechanical properties of an as-cast Ni$_{3}$Al alloy (IC221M) at operation temperature, 900 °C. Solution heat treatment was hypothesized to have beneficial effects through dissolving γ Ni$_{5}$Zr eutectic into the matrix. The microstructures, oxidation behavior in air at 900 °C, and mechanical properties with aging times at 900 °C were examined after solution heat treatment of as-cast Ni$_{3}$Al alloy in Ar for up to 100 h at 1100 °C. The oxide penetration depth into the matrix was dramatically decreased and more homogeneous surface oxides were obtained relative to the no solution, treatment case. Hardness was improved by solution heat treatment due to a solid solution strengthening effect by Zr, but the tensile properties after solution heat treatment were not significantly different from those prior to treatment.
ISSN 15989623
Age Range 18 to 22 years ♦ above 22 year
Educational Use Research
Education Level UG and PG
Learning Resource Type Article
Publisher Date 2006-01-01
Publisher Place Seoul
Journal Metals and Materials
Volume Number 12
Issue Number 2
Page Count 7
Starting Page 153
Ending Page 159

Open content in new tab

   Open content in new tab
Source: SpringerLink